附录1：外文原文
The machinability of material
The machinability of a material usually defined in terms of four factors:
（1）. Surface finish and integrity of the machined part;
（2）. Tool life obtained;
（3）. Force and power requirements;
（4）. Chip control.
Thus, good machinability good surface finish and integrity, long tool life, and low force And power requirements. As for chip control, long and thin (stringy) cured chips, if not broken up, can severely interfere with the cutting operation by becoming entangled in the cutting zone.
Because of the complex nature of cutting operations, it is difficult to establish relationships that quantitatively define the machinability of a material. In manufacturing plants, tool life and surface roughness are generally considered to be the most important factors in machinability. Although not used much any more, approximate machinability ratings are available in the example below.
1. Machinability Of Steels
Because steels are among the most important engineering materials , their machinability has been studied extensively. The machinability of steels has been mainly improved by adding lead and sulfur to obtain so-called free-machining steels.
Resulfurized and Rephosphorized steels. Sulfur in steels forms manganese sulfide inclusions (second-phase particles), which act as stress raisers in the primary shear zone. As a result, the chips produced break up easily and are small; this improves machinability. The size, shape, distribution, and concentration of these inclusions significantly influence machinability. Elements such as tellurium and selenium, which are both chemically similar to sulfur, act as inclusion modifiers in resulfurized steels.
Phosphorus in steels has two major effects. It strengthens the ferrite, causing increased hardness. Harder steels result in better chip formation and surface finish.
Note that soft steels can be difficult to machine, with built-up edge formation and poor surface finish. The second effect is that increased hardness causes the formation of short chips instead of continuous stringy ones, thereby improving machinability.
Leaded Steels. A high percentage of lead in steels solidifies at the tip of manganese sulfide inclusions. In non-resulfurized grades of steel, lead takes the form of dispersed fine particles. Lead is insoluble in iron, copper, and aluminum and their alloys. Because of its low shear strength, therefore, lead acts as a solid lubricant and is smeared over the tool-chip interface during cutting. This behavior has been verified by the presence of high concentrations of lead on the tool-side face of chips when machining leaded steels.
When the temperature is sufficiently high-for instance, at high cutting speeds and feeds —the lead melts directly in front of the tool, acting as a liquid lubricant. In addition to this effect, lead lowers the shear stress in the primary shear zone, reducing cutting forces and power consumption. Lead can be used in every grade of steel, such as 10xx, 11xx, 12xx, 41xx, etc. Leaded steels are identified by the letter L between the second and third numerals (for example, 10L45). (Note that in stainless steels, similar use of the letter L means “low carbon,” a condition that improves their corrosion resistance.)
However, because lead is a well-known toxin and a pollutant, there are serious environmental concerns about its use in steels (estimated at 4500 tons of lead consumption every year in the production of steels). Consequently, there is a continuing trend toward eliminating the use of lead in steels (lead-free steels). Bismuth and tin are now being investigated as possible substitutes for lead in steels.
Calcium-Deoxidized Steels. An important development is calcium-deoxidized steels, in which oxide flakes of calcium silicates (CaSo) are formed. These flakes, in turn, reduce the strength of the secondary shear zone, decreasing tool-chip interface and wear. Temperature is correspondingly reduced. Consequently, these steels produce less crater wear, especially at high cutting speeds.
Stainless Steels. Austenitic (300 series) steels are generally difficult to machine. Chatter can be s problem, necessitating machine tools with high stiffness. However, ferritic stainless steels (also 300 series) have good machinability. Martensitic (400
series) steels are abrasive, tend to form a built-up edge, and require tool materials with high hot hardness and crater-wear resistance. Precipitation-hardening stainless steels are strong and abrasive, requiring hard and abrasion-resistant tool materials.
The Effects of Other Elements in Steels on Machinability. The presence of aluminum and silicon in steels is always harmful because these elements combine with oxygen to form aluminum oxide and silicates, which are hard and abrasive. These compounds increase tool wear and reduce machinability. It is essential to produce and use clean steels.
Carbon and manganese have various effects on the machinability of steels, depending on their composition. Plain low-carbon steels (less than 0.15% C) can produce poor surface finish by forming a built-up edge. Cast steels are more abrasive, although their machinability is similar to that of wrought steels. Tool and die steels are very difficult to machine and usually require annealing prior to machining. Machinability of most steels is improved by cold working, which hardens the material and reduces the tendency for built-up edge formation.
Other alloying elements, such as nickel, chromium, molybdenum, and vanadium, which improve the properties of steels, generally reduce machinability. The effect of boron is negligible. Gaseous elements such as hydrogen and nitrogen can have particularly detrimental effects on the properties of steel. Oxygen has been shown to have a strong effect on the aspect ratio of the manganese sulfide inclusions; the higher the oxygen content, the lower the aspect ratio and the higher the machinability.
In selecting various elements to improve machinability, we should consider the possible detrimental effects of these elements on the properties and strength of the machined part in service. At elevated temperatures, for example, lead causes embrittlement of steels (liquid-metal embrittlement, hot shortness), although at room temperature it has no effect on mechanical properties.
Sulfur can severely reduce the hot workability of steels, because of the formation of iron sulfide, unless sufficient manganese is present to prevent such formation. At room temperature, the mechanical properties of resulfurized steels depend on the orientation of the deformed manganese sulfide inclusions (anisotropy). Rephosphorized steels are significantly less ductile, and are produced solely to
improve machinability.
2. Machinability of Various Other Metals
Aluminum is generally very easy to machine, although the softer grades tend to form a built-up edge, resulting in poor surface finish. High cutting speeds, high rake angles, and high relief angles are recommended. Wrought aluminum alloys with high silicon content and cast aluminum alloys may be abrasive; they require harder tool materials. Dimensional tolerance control may be a problem in machining aluminum, since it has a high thermal coefficient of expansion and a relatively low elastic modulus.
Beryllium is similar to cast irons. Because it is more abrasive and toxic, though, it requires machining in a controlled environment.
Cast gray irons are generally machinable but are. Free carbides in castings reduce their machinability and cause tool chipping or fracture, necessitating tools with high toughness. Nodular and malleable irons are machinable with hard tool materials.
Cobalt-based alloys are abrasive and highly work-hardening. They require sharp, abrasion-resistant tool materials and low feeds and speeds.
Wrought copper can be difficult to machine because of built-up edge formation, although cast copper alloys are easy to machine. Brasses are easy to machine, especially with the addition pf lead (leaded free-machining brass). Bronzes are more difficult to machine than brass.
Magnesium is very easy to machine, with good surface finish and prolonged tool life. However care should be exercised because of its high rate of oxidation and the danger of fire (the element is pyrophoric).
Molybdenum is ductile and work-hardening, so it can produce poor surface finish. Sharp tools are necessary.
Nickel-based alloys are work-hardening, abrasive, and strong at high temperatures. Their machinability is similar to that of stainless steels.
Tantalum is very work-hardening, ductile, and soft. It produces a poor surface finish; tool wear is high.
Titanium and its alloys have poor thermal conductivity (indeed, the lowest of all metals), causing significant temperature rise and built-up edge; they can be difficult to
machine.
Tungsten is brittle, strong, and very abrasive, so its machinability is low, although it greatly improves at elevated temperatures.
Zirconium has good machinability. It requires a coolant-type cutting fluid, however, because of the explosion and fire.
3. Machinability of Various Materials
Graphite is abrasive; it requires hard, abrasion-resistant, sharp tools.
Thermoplastics generally have low thermal conductivity, low elastic modulus, and low softening temperature. Consequently, machining them requires tools with positive rake angles (to reduce cutting forces), large relief angles, small depths of cut and feed, relatively high speeds, and
proper support of the workpiece. Tools should be sharp.
External cooling of the cutting zone may be necessary to keep the chips from becoming “gummy” and sticking to the tools. Cooling can usually be achieved with a jet of air, vapor mist, or water-soluble oils. Residual stresses may develop during machining. To relieve these stresses, machined parts can be annealed for a period of time at temperatures ranging from C ?80 to C ?160 (F ?175to F ?315), and then cooled slowly and uniformly to room temperature.
Thermosetting plastics are brittle and sensitive to thermal gradients during cutting. Their machinability is generally similar to that of thermoplastics.
Because of the fibers present, reinforced plastics are very abrasive and are difficult to machine. Fiber tearing, pulling, and edge delamination are significant problems; they can lead to severe reduction in the load-carrying capacity of the component. Furthermore, machining of these materials requires careful removal of machining debris to avoid contact with and inhaling of the fibers.
The machinability of ceramics has improved steadily with the development of nanoceramics and with the selection of appropriate processing parameters, such as ductile-regime cutting .
Metal-matrix and ceramic-matrix composites can be difficult to machine, depending on the properties of the individual components, i.e., reinforcing or whiskers, as well as the matrix material.
4. Thermally Assisted Machining
Metals and alloys that are difficult to machine at room temperature can be machined more easily at elevated temperatures. In thermally assisted machining (hot machining), the source of heat—a torch, induction coil, high-energy beam (such as laser or electron beam), or plasma arc—is forces, (b) increased tool life, (c) use of inexpensive cutting-tool materials, (d) higher material-removal rates, and (e) reduced tendency for vibration and chatter.
It may be difficult to heat and maintain a uniform temperature distribution within the workpiece. Also, the original microstructure of the workpiece may be adversely affected by elevated temperatures. Most applications of hot machining are in the turning of high-strength metals and alloys, although experiments are in progress to machine ceramics such as silicon nitride.
SUMMARY
Machinability is usually defined in terms of surface finish, tool life, force and power requirements, and chip control. Machinability of materials depends not only on their intrinsic properties and microstructure, but also on proper selection and control of process variables.
附录2：外文中文翻译
材料的可机加工性
一种材料的可机加工性通常以四种因素的方式定义：
（1）、分的表面光洁性和表面完整性。
（2）、刀具的寿命。
（3）、切削力和功率的需求。
（4）、切屑控制。
以这种方式，好的可机加工性指的是好的表面光洁性和完整性，长的刀具寿命，低的切削力和功率需求。关于切屑控制，细长的卷曲切屑，如果没有被切割成小片，以在切屑区变的混乱，缠在一起的方式能够严重的介入剪切工序。
因为剪切工序的复杂属性，所以很难建立定量地释义材料的可机加工性的关系。在制造厂里，刀具寿命和表面粗糙度通常被认为是可机加工性中最重要的因素。尽管已不再大量的被使用，近乎准确的机加工率在以下的例子中能够被看到。
1.钢的可机加工性
因为钢是最重要的工程材料之一，所以他们的可机加工性已经被广泛地研究过。通过宗教铅和硫磺，钢的可机加工性已经大大地提高了。从而得到了所谓的易切削钢。
二次硫化钢和二次磷化钢硫在钢中形成硫化锰夹杂物（第二相粒子），这些夹杂物在第一剪切区引起应力。其结果是使切屑容易断开而变小，从而改善了可加工性。这些夹杂物的大小、形状、分布和集中程度显著的影响可加工性。化学元素如碲和硒，其化学性质与硫类似，在二次硫化钢中起夹杂物改性作用。
钢中的磷有两个主要的影响。它加强铁素体，增加硬度。越硬的钢，形成更好的切屑形成和表面光洁性。需要注意的是软钢不适合用于有积屑瘤形成和很差的表面光洁性的机器。第二个影响是增加的硬度引起短切屑而不是不断的细长的切屑的形成，因此提高可加工性。
含铅的钢钢中高含量的铅在硫化锰夹杂物尖端析出。在非二次硫化钢中，铅呈细小而分散的颗粒。铅在铁、铜、铝和它们的合金中是不能溶解的。因为它的低抗剪强度。因此，铅充当固体润滑剂并且在切削时，被涂在刀具和切屑的接口处。这一特性已经被在机加工铅钢时，在切屑的刀具面表面有高浓度的铅的存在所证实。
当温度足够高时—例如，在高的切削速度和进刀速度下—铅在刀具前直接熔化，并且充当液体润滑剂。除了这个作用，铅降低第一剪切区中的剪应力，减小切削力和功率消耗。铅能用于各种钢号，例如10XX，11XX，12XX，41XX等等。
铅钢被第二和第三数码中的字母L所识别（例如，10L45）。（需要注意的是在不锈钢中，字母L的相同用法指的是低碳，提高它们的耐蚀性的条件）。
然而，因为铅是有名的毒素和污染物，因此在钢的使用中存在着严重的环境隐患（在钢产品中每年大约有4500吨的铅消耗）。结果，对于估算钢中含铅量的使用存在一个持续的趋势。铋和锡现正作为钢中的铅最可能的替代物而被人们所研究。
脱氧钙钢一个重要的发展是脱氧钙钢，在脱氧钙钢中矽酸钙盐中的氧化物片的形成。这些片状，依次减小第二剪切区中的力量，降低刀具和切屑接口处的摩擦和磨损。温度也相应地降低。结果，这些钢产生更小的月牙洼磨损，特别是在高切削速度时更是如此。
不锈钢奥氏体钢通常很难机加工。振动能成为一个问题，需要有高硬度的机床。然而，铁素体不锈钢有很好的可机加工性。马氏体钢易磨蚀，易于形成积屑瘤，并且要求刀具材料有高的热硬度和耐月牙洼磨损性。经沉淀硬化的不锈钢强度高、磨蚀性强，因此要求刀具材料硬而耐磨。
钢中其它元素在可机加工性方面的影响钢中铝和矽的存在总是有害的，因为这些元素结合氧会生成氧化铝和矽酸盐，而氧化铝和矽酸盐硬且具有磨蚀性。这些化合物增加刀具磨损，降低可机加工性。因此生产和使用净化钢非常必要。
根据它们的构成，碳和锰钢在钢的可机加工性方面有不同的影响。低碳素钢（少于0.15%的碳）通过形成一个积屑瘤能生成很差的表面光洁性。尽管铸钢的可机加工性和锻钢的大致相同，但铸钢具有更大的磨蚀性。刀具和模具钢很难用于机加工，他们通常再煅烧后再机加工。大多数钢的可机加工性在冷加工后都有所提高，冷加工能使材料变硬并且减少积屑瘤的形成。
其它合金元素，例如镍、铬、钳和钒，能提高钢的特性，减小可机加工性。硼的影响可以忽视。气态元素比如氢和氮在钢的特性方面能有特别的有害影响。氧已经被证明了在硫化锰夹杂物的纵横比方面有很强的影响。越高的含氧量，就产生越低的纵横比和越高的可机加工性。
选择各种元素以改善可加工性，我们应该考虑到这些元素对已加工零件在使用中的性能和强度的不利影响。例如，当温度升高时，铝会使钢变脆（液体—金属脆化，热脆化），尽管其在室温下对力学性能没有影响。
因为硫化铁的构成，硫能严重的减少钢的热加工性，除非有足够的锰来防止这种结构的形成。在室温下，二次磷化钢的机械性能依赖于变形的硫化锰夹杂物的定位（各向异性）。二次磷化钢具有更小的延展性，被单独生成来提高机加工性。
2.其它不同金属的机加工性
尽管越软的品种易于生成积屑瘤，但铝通常很容易被机加工，导致了很差的表面光洁性。高的切削速度，高的前角和高的后角都被推荐了。有高含量的矽的锻铝合金铸铝合金也许具有磨蚀性，它们要求更硬的刀具材料。尺寸公差控制也许在机加工铝时会成为一个问题，因为它有膨胀的高导热系数和相对低的弹性模数。
铍和铸铁相同。因为它更具磨蚀性和毒性，尽管它要求在可控人工环境下进行机加工。
灰铸铁普遍地可加工，但也有磨蚀性。铸造无中的游离碳化物降低它们的可机加工性，引起刀具切屑或裂口。它需要具有强韧性的工具。具有坚硬的刀具材料的球墨铸铁和韧性铁是可加工的。
钴基合金有磨蚀性且高度加工硬化的。它们要求尖的且具有耐蚀性的刀具材料并且有低的走刀和速度。
尽管铸铜合金很容易机加工，但因为锻铜的积屑瘤形成因而锻铜很难机加工。黄铜很容易机加工，特别是有添加的铅更容易。青铜比黄铜更难机加工。
镁很容易机加工，镁既有很好的表面光洁性和长久的刀具寿命。然而，因为高的氧化速度和火种的危险（这种元素易燃），因此我们应该特别小心使用它。
钳易拉长且加工硬化，因此它生成很差的表面光洁性。尖的刀具是很必要的。
镍基合金加工硬化，具有磨蚀性，且在高温下非常坚硬。它的可机加工性和不锈钢相同。
钽非常的加工硬化，具有可延性且柔软。它生成很差的表面光洁性且刀具磨损非常大。
钛和它的合金导热性(的确，是所有金属中最低的)，因此引起明显的温度升高和积屑瘤。它们是难机加工的。
钨易脆，坚硬，且具有磨蚀性，因此尽管它的性能在高温下能大大提高，但它的机加工性仍很低。
锆有很好的机加工性。然而，因为有爆炸和火种的危险性，它要求有一个冷却性质好的切削液。
3.各种材料的机加工性
石墨具有磨蚀性。它要求硬的、尖的，具有耐蚀性的刀具。
塑性塑料通常有低的导热性，低的弹性模数和低的软化温度。因此，机加工热塑性塑料要求有正前角的刀具（以此降低切削力），还要求有大的后角，小的切削和走刀深的，相对高的速度和工件的正确支承。刀具应该很尖。
切削区的外部冷却也许很必要，以此来防止切屑变的有黏性且粘在刀具上。
有了空气流，汽雾或水溶性油，通常就能实现冷却。在机加工时，残余应力也许能生成并发展。为了解除这些力，已机加工的部分要在C
C ??16080—（F F ??315175—）的温度范围内冷却一段时间，然而慢慢地无变化地冷却到室温。
热固性塑料易脆，并且在切削时对热梯度很敏感。它的机加工性和热塑性塑料的相同。
因为纤维的存在，加强塑料具有磨蚀性，且很难机加工。纤维的撕裂、拉出和边界分层是非常严重的问题。它们能导致构成要素的承载能力大大下降。而且，这些材料的机加工要求对加工残片仔细切除，以此来避免接触和吸进纤维。
随着纳米陶瓷的发展和适当的参数处理的选择，例如塑性切削,陶瓷器的可机加工性已大大地提高了。
金属基复合材料和陶瓷基复合材料很能机加工，它们依赖于单独的成分的特性，比如说增强纤维或金属须和基体材料。
4.热辅助加工
在室温下很难机加工的金属和合金在高温下能更容易地机加工。在热辅助加工时（高温切削），热源—一个火把，感应线圈，高能束流（例如雷射或电子束），或等离子弧—被集中在切削刀具前的一块区域内。好处是：（a ）低的切削力。（b ）增加的刀具寿命。（c ）便宜的切削刀具材料的使用。（d ）更高的材料切除率。（e ）减少振动。
也许很难在工件内加热和保持一个不变的温度分布。而且，工件的最初微观结构也许被高温影响，且这种影响是相当有害的。尽管实验在进行中，以此来机加工陶瓷器如氮化矽，但高温切削仍大多数应用在高强度金属和高温度合金的车削中。
小结
通常，零件的可机加工性能是根据以下因素来定义的：表面粗糙度，刀具的寿命，切削力和功率的需求以及切屑的控制。材料的可机加工性能不仅取决于起内在特性和微观结构，而且也依赖于工艺参数的适当选择与控制。
外文出处： 《Exploiting Software How to Break Code》By Greg Hoglund, Gary McGraw Publisher : Addison Wesley Pub Date : February 17, 2004 ISBN : 0-201-78695-8 译文标题： JDBC接口技术 译文： JDBC是一种可用于执行SQL语句的JavaAPI（ApplicationProgrammingInterface应用程序设计接口）。它由一些Java语言编写的类和界面组成。JDBC为数据库应用开发人员、数据库前台工具开发人员提供了一种标准的应用程序设计接口，使开发人员可以用纯Java语言编写完整的数据库应用程序。 一、ODBC到JDBC的发展历程 说到JDBC，很容易让人联想到另一个十分熟悉的字眼“ODBC”。它们之间有没有联系呢？如果有，那么它们之间又是怎样的关系呢？ ODBC是OpenDatabaseConnectivity的英文简写。它是一种用来在相关或不相关的数据库管理系统（DBMS）中存取数据的，用C语言实现的，标准应用程序数据接口。通过ODBCAPI，应用程序可以存取保存在多种不同数据库管理系统（DBMS）中的数据，而不论每个DBMS使用了何种数据存储格式和编程接口。 1．ODBC的结构模型 ODBC的结构包括四个主要部分：应用程序接口、驱动器管理器、数据库驱动器和数据源。应用程序接口：屏蔽不同的ODBC数据库驱动器之间函数调用的差别，为用户提供统一的SQL编程接口。 驱动器管理器：为应用程序装载数据库驱动器。 数据库驱动器：实现ODBC的函数调用，提供对特定数据源的SQL请求。如果需要，数据库驱动器将修改应用程序的请求，使得请求符合相关的DBMS所支持的文法。 数据源：由用户想要存取的数据以及与它相关的操作系统、DBMS和用于访问DBMS的网络平台组成。 虽然ODBC驱动器管理器的主要目的是加载数据库驱动器，以便ODBC函数调用，但是数据库驱动器本身也执行ODBC函数调用，并与数据库相互配合。因此当应用系统发出调用与数据源进行连接时，数据库驱动器能管理通信协议。当建立起与数据源的连接时，数据库驱动器便能处理应用系统向DBMS发出的请求，对分析或发自数据源的设计进行必要的翻译，并将结果返回给应用系统。 2．JDBC的诞生 自从Java语言于1995年5月正式公布以来，Java风靡全球。出现大量的用java语言编写的程序，其中也包括数据库应用程序。由于没有一个Java语言的API，编程人员不得不在Java程序中加入C语言的ODBC函数调用。这就使很多Java的优秀特性无法充分发挥，比如平台无关性、面向对象特性等。随着越来越多的编程人员对Java语言的日益喜爱，越来越多的公司在Java程序开发上投入的精力日益增加，对java语言接口的访问数据库的API 的要求越来越强烈。也由于ODBC的有其不足之处，比如它并不容易使用，没有面向对象的特性等等，SUN公司决定开发一Java语言为接口的数据库应用程序开发接口。在JDK1．x 版本中，JDBC只是一个可选部件，到了JDK1．1公布时，SQL类包（也就是JDBCAPI）
前言 在目前激烈的市场竞争中，产品投入市场的迟早往往是成败的关键。模具是高质量、高效率的产品生产工具，模具开发周期占整个产品开发周期的主要部分。因此客户对模具开发周期要求越来越短，不少客户把模具的交货期放在第一位置，然后才是质量和价格。因此，如何在保证质量、控制成本的前提下加工模具是值得认真考虑的问题。模具加工工艺是一项先进的制造工艺，已成为重要发展方向，在航空航天、汽车、机械等各行业得到越来越广泛的应用。模具加工技术，可以提高制造业的综合效益和竞争力。研究和建立模具工艺数据库，为生产企业提供迫切需要的高速切削加工数据，对推广高速切削加工技术具有非常重要的意义。本文的主要目标就是构建一个冲压模具工艺过程，将模具制造企业在实际生产中结合刀具、工件、机床与企业自身的实际情况积累得高速切削加工实例、工艺参数和经验等数据有选择地存储到高速切削数据库中，不但可以节省大量的人力、物力、财力，而且可以指导高速加工生产实践，达到提高加工效率，降低刀具费用，获得更高的经济效益。 1.冲压的概念、特点及应用 冲压是利用安装在冲压设备（主要是压力机）上的模具对材料施加压力，使其产生分离或塑性变形，从而获得所需零件（俗称冲压或冲压件）的一种压力加工方法。冲压通常是在常温下对材料进行冷变形加工，且主要采用板料来加工成所需零件，所以也叫冷冲压或板料冲压。冲压是材料压力加工或塑性加工的主要方法之一，隶属于材料成型工程术。 冲压所使用的模具称为冲压模具，简称冲模。冲模是将材料（金属或非金属）批量加工成所需冲件的专用工具。冲模在冲压中至关重要，没有符合要求的冲模，批量冲压生产就难以进行；没有先进的冲模，先进的冲压工艺就无法实现。冲压工艺与模具、冲压设备和冲压材料构成冲压加工的三要素，只有它们相互结合才能得出冲压件。 与机械加工及塑性加工的其它方法相比，冲压加工无论在技术方面还是经济方面都具有许多独特的优点，主要表现如下； (1) 冲压加工的生产效率高，且操作方便，易于实现机械化与自动化。这是
Load and Ultimate Moment of Prestressed Concrete Action Under Overload-Cracking Load It has been shown that a variation in the external load acting on a prestressed beam results in a change in the location of the pressure line for beams in the elastic range.This is a fundamental principle of prestressed construction.In a normal prestressed beam,this shift in the location of the pressure line continues at a relatively uniform rate,as the external load is increased,to the point where cracks develop in the tension fiber.After the cracking load has been exceeded,the rate of movement in the pressure line decreases as additional load is applied,and a significant increase in the stress in the prestressing tendon and the resultant concrete force begins to take place.This change in the action of the internal moment continues until all movement of the pressure line ceases.The moment caused by loads that are applied thereafter is offset entirely by a corresponding and proportional change in the internal forces,just as in reinforced-concrete construction.This fact,that the load in the elastic range and the plastic range is carried by actions that are fundamentally different,is very significant and renders strength computations essential for all designs in order to ensure that adequate safety factors exist.This is true even though the stresses in the elastic range may conform to a recognized elastic design criterion. It should be noted that the load deflection curve is close to a straight line up to the cracking load and that the curve becomes progressively more curved as the load is increased above the cracking load.The curvature of the load-deflection curve for loads over the cracking load is due to the change in the basic internal resisting moment action that counteracts the applied loads,as described above,as well as to plastic strains that begin to take place in the steel and the concrete when stressed to high levels. In some structures it may be essential that the flexural members remain crack free even under significant overloads.This may be due to the structures’being exposed to exceptionally corrosive atmospheres during their useful life.In designing prestressed members to be used in special structures of this type,it may be necessary to compute the load that causes cracking of the tensile flange,in order to ensure that adequate safety against cracking is provided by the design.The computation of the moment that will cause cracking is also necessary to ensure compliance with some design criteria. Many tests have demonstrated that the load-deflection curves of prestressed beams are approximately linear up to and slightly in excess of the load that causes the first cracks in the tensile flange.(The linearity is a function of the rate at which the load is applied.)For this reason,normal elastic-design relationships can be used in computing the cracking load by simply determining the load that results in a net tensile stress in the tensile flange(prestress minus the effects of the applied loads)that is equal to the tensile strength of the concrete.It is customary to assume that the flexural tensile strength of the concrete is equal to the modulus of rupture of the
附录一英文科技文献翻译 英文原文： Experimental investigation of laser surface textured parallel thrust bearings Performance enhancements by laser surface texturing (LST) of parallel-thrust bearings is experimentally investigated. Test results are compared with a theoretical model and good correlation is found over the relevant operating conditions. A compari- son of the performance of unidirectional and bi-directional partial-LST bearings with that of a baseline, untextured bearing is presented showing the bene?ts of LST in terms of increased clearance and reduced friction. KEY WORDS: ?uid ?lm bearings, slider bearings, surface texturing 1. Introduction The classical theory of hydrodynamic lubrication yields linear (Couette) velocity distribution with zero pressure gradients between smooth parallel surfaces under steady-state sliding. This results in an unstable hydrodynamic ?lm that would collapse under any external force acting normal to the surfaces. However, experience shows that stable lubricating ?lms can develop between parallel sliding surfaces, generally because of some mechanism that relaxes one or more of the assumptions of the classical theory. A stable ?uid ?lm with su?cient load-carrying capacity in parallel sliding surfaces can be obtained, for example, with macro or micro surface structure of di?erent types. These include waviness [1] and protruding microasperities [2–4]. A good literature review on the subject can be found in Ref. [5]. More recently, laser surface texturing (LST) [6–8], as well as inlet roughening by longitudinal or transverse grooves [9] were suggested to provide load capacity in parallel sliding. The inlet roughness concept of Tonder [9] is based on ??e?ective clearance‘‘ reduction in the sliding direction and in this respect it is identical to the par- tial-LST concept described in ref. [10] for generating hydrostatic e?ect in high-pressure mechanical seals. Very recently Wang et al. [11] demonstrated experimentally a doubling of the load-carrying capacity for the surface- texture design by reactive ion etching of SiC
毕业设计（论文）外文文献翻译 文献、资料中文题目：软件开发概念和设计方法文献、资料英文题目： 文献、资料来源： 文献、资料发表（出版）日期： 院（部）： 专业： 班级： 姓名： 学号： 指导教师： 翻译日期： 2017.02.14
外文资料原文 Software Development Concepts and Design Methodologies During the 1960s, ma inframes and higher level programming languages were applied to man y problems including human resource s yste ms,reservation s yste ms, and manufacturing s yste ms. Computers and software were seen as the cure all for man y bu siness issues were some times applied blindly. S yste ms sometimes failed to solve the problem for which the y were designed for man y reasons including: ?Inability to sufficiently understand complex problems ?Not sufficiently taking into account end-u ser needs, the organizational environ ment, and performance tradeoffs ?Inability to accurately estimate development time and operational costs ?Lack of framework for consistent and regular customer communications At this time, the concept of structured programming, top-down design, stepwise refinement，and modularity e merged. Structured programming is still the most dominant approach to software engineering and is still evo lving. These failures led to the concept of "software engineering" based upon the idea that an engineering-like discipl ine could be applied to software design and develop ment. Software design is a process where the software designer applies techniques and principles to produce a conceptual model that de scribes and defines a solution to a problem. In the beginning, this des ign process has not been well structured and the model does not alwa ys accurately represent the problem of software development. However,design methodologies have been evolving to accommo date changes in technolog y coupled with our increased understanding of development processes. Whereas early desig n methods addressed specific aspects of the
机械设计理论 机械设计是一门通过设计新产品或者改进老产品来满足人类需求的应用技术科学。它涉及工程技术的各个领域，主要研究产品的尺寸、形状和详细结构的基本构思，还要研究产品在制造、销售和使用等方面的问题。 进行各种机械设计工作的人员通常被称为设计人员或者机械设计工程师。机械设计是一项创造性的工作。设计工程师不仅在工作上要有创造性，还必须在机械制图、运动学、工程材料、材料力学和机械制造工艺学等方面具有深厚的基础知识。如前所诉，机械设计的目的是生产能够满足人类需求的产品。发明、发现和科技知识本身并不一定能给人类带来好处，只有当它们被应用在产品上才能产生效益。因而，应该认识到在一个特定的产品进行设计之前，必须先确定人们是否需要这种产品。 应当把机械设计看成是机械设计人员运用创造性的才能进行产品设计、系统分析和制定产品的制造工艺学的一个良机。掌握工程基础知识要比熟记一些数据和公式更为重要。仅仅使用数据和公式是不足以在一个好的设计中做出所需的全部决定的。另一方面，应该认真精确的进行所有运算。例如，即使将一个小数点的位置放错，也会使正确的设计变成错误的。 一个好的设计人员应该勇于提出新的想法，而且愿意承担一定的风险，当新的方法不适用时，就使用原来的方法。因此，设计人员必须要有耐心，因为所花费的时间和努力并不能保证带来成功。一个全新的设计，要求屏弃许多陈旧的，为人们所熟知的方法。由于许多人墨守成规，这样做并不是一件容易的事。一位机械设计师应该不断地探索改进现有的产品的方法，在此过程中应该认真选择原有的、经过验证的设计原理，将其与未经过验证的新观念结合起来。 新设计本身会有许多缺陷和未能预料的问题发生，只有当这些缺陷和问题被解决之后，才能体现出新产品的优越性。因此，一个性能优越的产品诞生的同时，也伴随着较高的风险。应该强调的是，如果设计本身不要求采用全新的方法，就没有必要仅仅为了变革的目的而采用新方法。 在设计的初始阶段，应该允许设计人员充分发挥创造性，不受各种约束。即使产生了许多不切实际的想法，也会在设计的早期，即绘制图纸之前被改正掉。只有这样，才不致于堵塞创新的思路。通常，要提出几套设计方案，然后加以比较。很有可能在最后选定的方案中，采用了某些未被接受的方案中的一些想法。
本科毕业论文(设计) 外文翻译 学院：机电工程学院 专业：机械工程及自动化 姓名：高峰 指导教师：李延胜 2011年05 月10日 教育部办公厅 Failure Analysis，Dimensional Determination And
Analysis，Applications Of Cams INTRODUCTION It is absolutely essential that a design engineer know how and why parts fail so that reliable machines that require minimum maintenance can be designed．Sometimes a failure can be serious，such as when a tire blows out on an automobile traveling at high speed．On the other hand，a failure may be no more than a nuisance．An example is the loosening of the radiator hose in an automobile cooling system．The consequence of this latter failure is usually the loss of some radiator coolant，a condition that is readily detected and corrected．The type of load a part absorbs is just as significant as the magnitude．Generally speaking，dynamic loads with direction reversals cause greater difficulty than static loads，and therefore，fatigue strength must be considered．Another concern is whether the material is ductile or brittle．For example，brittle materials are considered to be unacceptable where fatigue is involved． Many people mistakingly interpret the word failure to mean the actual breakage of a part．However，a design engineer must consider a broader understanding of what appreciable deformation occurs．A ductile material，however will deform a large amount prior to rupture．Excessive deformation，without fracture，may cause a machine to fail because the deformed part interferes with a moving second part．Therefore，a part fails(even if it has not physically broken)whenever it no longer fulfills its required function．Sometimes failure may be due to abnormal friction or vibration between two mating parts．Failure also may be due to a phenomenon called creep，which is the plastic flow of a material under load at elevated temperatures．In addition，the actual shape of a part may be responsible for failure．For example，stress concentrations due to sudden changes in contour must be taken into account．Evaluation of stress considerations is especially important when there are dynamic loads with direction reversals and the material is not very ductile． In general，the design engineer must consider all possible modes of failure，which include the following． ——Stress ——Deformation ——Wear ——Corrosion ——Vibration ——Environmental damage ——Loosening of fastening devices
外文翻译 专业机械设计制造及其自动化学生姓名刘链柱 班级机制111 学号1110101102 指导教师葛友华
外文资料名称： Design and performance evaluation of vacuum cleaners using cyclone technology 外文资料出处：Korean J. Chem. Eng., 23(6), (用外文写) 925-930 (2006) 附件： 1.外文资料翻译译文 2.外文原文
应用旋风技术真空吸尘器的设计和性能介绍 吉尔泰金，洪城铱昌，宰瑾李， 刘链柱译 摘要：旋风型分离器技术用于真空吸尘器 - 轴向进流旋风和切向进气道流旋风有效地收集粉尘和降低压力降已被实验研究。优化设计等因素作为集尘效率，压降，并切成尺寸被粒度对应于分级收集的50％的效率进行了研究。颗粒切成大小降低入口面积，体直径，减小涡取景器直径的旋风。切向入口的双流量气旋具有良好的性能考虑的350毫米汞柱的低压降和为1.5μm的质量中位直径在1米3的流量的截止尺寸。一使用切向入口的双流量旋风吸尘器示出了势是一种有效的方法，用于收集在家庭中产生的粉尘。 摘要及关键词：吸尘器; 粉尘; 旋风分离器 引言 我们这个时代的很大一部分都花在了房子，工作场所，或其他建筑，因此，室内空间应该是既舒适情绪和卫生。但室内空气中含有超过室外空气因气密性的二次污染物，毒物，食品气味。这是通过使用产生在建筑中的新材料和设备。真空吸尘器为代表的家电去除有害物质从地板到地毯所用的商用真空吸尘器房子由纸过滤，预过滤器和排气过滤器通过洁净的空气排放到大气中。虽然真空吸尘器是方便在使用中，吸入压力下降说唱空转成比例地清洗的时间，以及纸过滤器也应定期更换，由于压力下降，气味和细菌通过纸过滤器内的残留粉尘。 图1示出了大气气溶胶的粒度分布通常是双峰形，在粗颗粒（>2.0微米）模式为主要的外部来源，如风吹尘，海盐喷雾，火山，从工厂直接排放和车辆废气排放，以及那些在细颗粒模式包括燃烧或光化学反应。表1显示模式，典型的大气航空的直径和质量浓度溶胶被许多研究者测量。精细模式在0.18?0.36 在5.7到25微米尺寸范围微米尺寸范围。质量浓度为2?205微克，可直接在大气气溶胶和 3.85至36.3μg/m3柴油气溶胶。
I / 11 本科毕业设计外文翻译 <2018届） 论文题目基于WEB 的J2EE 的信息系统的方法研究 作者姓名[单击此处输入姓名] 指导教师[单击此处输入姓名] 学科(专业 > 所在学院计算机科学与技术学院 提交日期[时间 ]
基于WEB的J2EE的信息系统的方法研究 摘要：本文介绍基于工程的Java开发框架背后的概念，并介绍它如何用于IT 工程开发。因为有许多相同设计和开发工作在不同的方式下重复，而且并不总是符合最佳实践，所以许多开发框架建立了。我们已经定义了共同关注的问题和应用模式，代表有效解决办法的工具。开发框架提供：<1）从用户界面到数据集成的应用程序开发堆栈；<2）一个架构，基本环境及他们的相关技术，这些技术用来使用其他一些框架。架构定义了一个开发方法，其目的是协助客户开发工程。 关键词：J2EE 框架WEB开发 一、引言 软件工具包用来进行复杂的空间动态系统的非线性分析越来越多地使用基于Web的网络平台，以实现他们的用户界面，科学分析，分布仿真结果和科学家之间的信息交流。对于许多应用系统基于Web访问的非线性分析模拟软件成为一个重要组成部分。网络硬件和软件方面的密集技术变革[1]提供了比过去更多的自由选择机会[2]。因此，WEB平台的合理选择和发展对整个地区的非线性分析及其众多的应用程序具有越来越重要的意义。现阶段的WEB发展的特点是出现了大量的开源框架。框架将Web开发提到一个更高的水平，使基本功能的重复使用成为可能和从而提高了开发的生产力。 在某些情况下，开源框架没有提供常见问题的一个解决方案。出于这个原因，开发在开源框架的基础上建立自己的工程发展框架。本文旨在描述是一个基于Java的框架，该框架利用了开源框架并有助于开发基于Web的应用。通过分析现有的开源框架，本文提出了新的架构，基本环境及他们用来提高和利用其他一些框架的相关技术。架构定义了自己开发方法，其目的是协助客户开发和事例工程。 应用程序设计应该关注在工程中的重复利用。即使有独特的功能要求，也
机械类外文翻译 塑料注塑模具浇口优化 摘要:用单注塑模具浇口位置的优化方法，本文论述。该闸门优化设计的目的是最大限度地减少注塑件翘曲变形，翘曲，是因为对大多数注塑成型质量问题的关键，而这是受了很大的部分浇口位置。特征翘曲定义为最大位移的功能表面到表面的特征描述零件翘曲预测长度比。结合的优化与数值模拟技术，以找出最佳浇口位置，其中模拟armealing算法用于搜索最优。最后，通过实例讨论的文件，它可以得出结论，该方法是有效的。 注塑模具、浇口位臵、优化、特征翘曲变形关键词: 简介 塑料注射成型是一种广泛使用的，但非常复杂的生产的塑料产品，尤其是具有高生产的要求，严密性，以及大量的各种复杂形状的有效方法。质量ofinjection 成型零件是塑料材料，零件几何形状，模具结构和工艺条件的函数。注塑模具的一个最重要的部分主要是以下三个组件集:蛀牙，盖茨和亚军，和冷却系统。拉米夫定、Seow(2000)、金和拉米夫定(2002) 通过改变部分的尼斯达到平衡的腔壁厚度。在平衡型腔充填过程提供了一种均匀分布压力和透射电镜,可以极大地减少高温的翘曲变形的部分～但仅仅是腔平衡的一个重要影响因素的一部分。cially Espe,部分有其功能上的要求,其厚度通常不应该变化。 pointview注塑模具设计的重点是一门的大小和位臵,以及流道系统的大小和布局。大门的大小和转轮布局通常被认定为常量。相对而言,浇口位臵与水口大小布局也更加灵活,可以根据不同的零件的质量。 李和吉姆(姚开屏,1996a)称利用优化流道和尺寸来平衡多流道系统为multiple 注射系统。转轮平衡被形容为入口压力的差异为一多型腔模具用相同的蛀牙,也存
河南科技学院新科学院 2013届本科毕业生论文（设计） 英文文献及翻译 Foreign capital inflows and welfare in an economy with imperfect competition 学生姓名：王艳杰 所在院系：经济系 所学专业：国际经济与贸易 导师姓名：侯黎杰 完成时间：2013年4月15日
Foreign capital inflows and welfare in an economy with imperfect competition Abstract:This paper examines the resource allocational and welfare effects of exogenous inflows of foreign capital in a general-equilibrium model with oligopolistic competition and unemployment. Although the welfare impact for the short run is ambiguous and dependent upon the strength of excess profits and scale economies relative to unemployment in manufacturing, in the long run additional inflows of foreign capital always improve national welfare with capital mobility. Hence, attracting foreign capital remains a sound policy for economies characterized by imperfect competition, scale economies,and regional unemployment. Keywords: International capital mobility; Imperfect competition; Welfare 1.Introduction The welfare effects of exogenous inflows of foreign capital in the presence of trade restrictions have been extensively studied. Brecher and Diaz Alejandro (1977) show that when imports are subject to tariffs, an introduction of fo reign capital inflows accentuates the tariff distortion and hence reduces national welfare if the import-competing sector is relatively capital-intensive. In contrast, Dei (1985) shows that when imports are restricted by quotas,foreign capital inflows in the presence of foreign-owned capital always improve welfare by depressing the rental and so lowering the payments to existing foreign-owned capital. Recently, Neary (1981), using a common framework for both tariffs and quotas, obtains more general results of foreign capital inflows; the welfare effect of such inflows depends crucially on whether foreign-owned capital exists initially in the home country. In addition, Khan (1982) and Grinols (1991) have examined the effects of foreign capital inflows for a generalized Harris-Todaro economy under tariff protection. Khan finds that the result by Brecher and Diaz Alejandro is still valid even in the presence of unemployment, whereas Grinols argues that increased foreign capital need not be detrimental to welfare if the opportunity costs of labor are sufficiently low. Noteworthy is that the models used by these authors are all based upon the premise of perfect competition along with constant returns-to-scale technology. Although perfect competition serves as a useful assumption in crystallizing theoretical insights, it nevertheless fails to depict many of the real-world phenomena. The real-world economy is characterized, to a large extent, by imperfect competition and economies of scale. The policy implications of imperfect competition and economies
沈阳工业大学工程学院 毕业设计（论文）外文翻译 毕业设计（论文）题目：工具盒盖注塑模具设计 外文题目：Friction , Lubrication of Bearing 译文题目：轴承的摩擦与润滑 系（部）：机械系 专业班级：机械设计制造及其自动化0801 学生姓名：王宝帅 指导教师：魏晓波 2010年10 月15 日
外文文献原文： Friction , Lubrication of Bearing In many of the problem thus far , the student has been asked to disregard or neglect friction . Actually , friction is present to some degree whenever two parts are in contact and move on each other. The term friction refers to the resistance of two or more parts to movement. Friction is harmful or valuable depending upon where it occurs. friction is necessary for fastening devices such as screws and rivets which depend upon friction to hold the fastener and the parts together. Belt drivers, brakes, and tires are additional applications where friction is necessary. The friction of moving parts in a machine is harmful because it reduces the mechanical advantage of the device. The heat produced by friction is lost energy because no work takes place. Also , greater power is required to overcome the increased friction. Heat is destructive in that it causes expansion. Expansion may cause a bearing or sliding surface to fit tighter. If a great enough pressure builds up because made from low temperature materials may melt. There are three types of friction which must be overcome in moving parts: (1)starting, (2)sliding, and(3)rolling. Starting friction is the friction between two solids that tend to resist movement. When two parts are at a state of rest, the surface irregularities of both parts tend to interlock and form a wedging action. To produce motion in these parts, the wedge-shaped peaks and valleys of the stationary surfaces must be made to slide out and over each other. The rougher the two surfaces, the greater is starting friction resulting from their movement . Since there is usually no fixed pattern between the peaks and valleys of two mating parts, the irregularities do not interlock once the parts are in motion but slide over each other. The friction of the two surfaces is known as sliding friction. As shown in figure ,starting friction is always greater than sliding friction . Rolling friction occurs when roller devces are subjected to tremendous stress which cause the parts to change shape or deform. Under these conditions, the material in front of a roller tends to pile up and forces the object to roll slightly uphill. This changing of shape , known as deformation, causes a movement of molecules. As a result ,heat is produced from the added energy required to keep the parts turning and overcome friction. The friction caused by the wedging action of surface irregularities can be overcome