中英文耐火材料国家标准
1 GB/T 2275-1987 镁砖及镁硅砖Magnesia and magnesia-silica refractory bricks
2 GB/T 2608-1987 硅砖Silica refractory bricks
3 GB/T 2988-1987 高铝砖High-alumina refractory bricks
4 GB/T 2997-1982 致密定形耐火制品显气孔率、吸水率、体积密度和真气孔率试验方法Test method for the apparent porosity, water absorption bulk density and true porosity of dense shaped refractory products
5 GB/T 2998-1982 定形隔热耐火制品体积密度和真气孔率试验方法Test method for bulk density and true porosity of shaped insulating refractory products
6 GB/T 2999-1982 粒状耐火材料体积密度试验方法Test method for the bulk density of granular refractory materials
7 GB/T 3000-1982 耐火制品透气度试验方法Test method for permeability of refractory products
8 GB/T 3001-1982 耐火制品常温抗折强度试验方法Test method for modulus of rupture of refractory products at room temperatures
9 GB/T 3002-1982 耐火制品高温抗折强度试验方法Test method for modulus of rupture of refractory products at elevated temperatures
10 GB/T 3003-1982 普通硅酸铝耐火纤维毡Ordinary alumino-silicate refractory fiber felts
11 GB/T 3004-1982 普通硅酸铝耐火纤维毡容重试验方法Test method for bulk density of ordinary alumino-silicate refractory fiber felts
12 GB/T 3005-1982 普通硅酸铝耐火纤维毡加热线收缩试验方法Test method for heating linear shrinkage of ordinary alumino-silicate refractory fiber felts
13 GB/T 3006-1982 普通硅酸铝耐火纤维毡渣球含量试验方法Test method for the content of slag ball of ordinary alumino-silicate refractory fiber felts
14 GB/T 3007-1982 普通硅酸铝耐火纤维毡含水量试验方法Test method for moisture content of ordinary alumino-silicate refractory fiber felts
15 GB/T 3008-1982 普通硅酸铝耐火纤维毡检验制样规定Rule for preparing samples of ordinary alumino-silicate refractory fiber felts
16 GB/T 3994-1983 粘土质隔热耐火砖Shaped insulating refractory products--Fireclay bricks
17 GB/T 3995-1983 高铝质隔热耐火砖Shaped insulating refractory products--High alumina bricks
18 GB/T 3996-1983 硅藻土隔热制品Shaped thermal insulating products--Diatomite bricks and shapes
19 GB/T 4513-1984 不定型耐火材料(致密和隔热) 分类Prepared unshaped refractory materials (dense and insulating)--Classification
20 GB/T 4984-1985 锆刚玉耐火材料化学分析方法Chemical analysis methods of zirconia-alumina refractories
21 GB/T 5069.1-1985 镁质耐火材料化学分析方法重量法测定灼烧失量Magnesite refractories--Determination of loss content on ignition--Gravimetric method
22 GB/T 5069.2-1985 镁质耐火材料化学分析方法钼蓝光度法测定二氧化硅量Magnesite refractories--Determination of silicon dioxide content--Molybdenum blue photometric method
23 GB/T 5069.3-1985 镁质耐火材料化学分析方法重量-钼蓝光度法测定二氧化硅量Magnesite refractories--Determination of silicon dioxide content--Gravimetric -molybdenum blue photometric method
24 GB/T 5069.4-1985 镁质耐火材料化学分析方法邻二氮杂菲光度法测定三氧化二铁量Magnesite refractories--Determination of iron oxide content--O-Phenanthroline photometric method
25 GB/T 5069.5-1985 镁质耐火材料化学分析方法铬天青S 光度法测定氧化铝量Magnesite refractories--Determination of aluminium oxide content--Chromazurol S photometric method
26 GB/T 5069.6-1985 镁质耐火材料化学分析方法EDTA容量法测定氧化铝量Magnesite refractories--Determination of aluminium oxide--EDTA volumetric method 27 GB/T 5069.7-1985 镁质耐火材料化学分析方法二安替比林甲烷光度法测定二氧化钛量Magnesite refractories--Determination of titanium dioxide content--Diantipyrylmethane photometric method
28 GB/T 5069.8-1985 镁质耐火材料化学分析方法EDTA容量法测定氧化钙量Magnesite refractories--Determination of calcium oxide content--EGTA volumetric method
29 GB/T 5069.9-1985 镁质耐火材料化学分析方法CyDTA容量法测定氧化镁量Magnesite refractories--Determination of magnesium oxide content--CyDTA volumetric method
30 GB/T 5069.10-1985 镁质耐火材料化学分析方法原子吸收分光光度法测定氧化锰量Magnesite refractories--Determination of manganese oxide content--Atomic absorption spectrophotometric method
31 GB/T 5069.11-1985 镁质耐火材料化学分析方法原子吸收分光光度法测定氧化钾、氧化钠量Magnesite refractories--Determination of potassium oxide and
sodium oxide contents--atomic absorption spectrophotometric method
32 GB/T 5070.1-1985 镁铬质耐火材料化学分析方法重量法测定灼烧失量Magnesite-chrome refractories--Determination of loss content on ignition--Gravimetric method
33 GB/T 5070.2-1985 镁铬质耐火材料化学分析方法钼蓝光度法测定二氧化硅量Magnesite-chrome refractories--Determination of silicon dioxide content--Molybdenum blue phetometric method
34 GB/T 5070.3-1985 镁铬质耐火材料化学分析方法邻二氮杂菲光度法测定三氧化二铁量Magnesite-chrome refractories--Determination of iron oxide content--O-Phenanthroline photometric method
35 GB/T 5070.4-1985 镁铬质耐火材料化学分析方法EDTA容量法测定氧化铝量Magnesite-chrome refractories--Determination of aluminium oxide--EDTA volumetric method
36 GB/T 5070.5-1985 镁铬质耐火材料化学分析方法二安替比林甲烷光度法测定二氧化钛量Magnesite-chrome refractories--Determination of titanium dioxide content--Diantipyrylmethane photometric method
37 GB/T 5070.6-1985 镁铬质耐火材料化学分析方法EGTA容量法测定氧化钙量Magnesite-chrome refractories--Determination of calcium oxide content--EGTA volumetric method
38 GB/T 5070.7-1985 镁铬质耐火材料化学分析方法CyDTA容量法测定氧化镁量Magnesite-chrome refractories--Determination of magnesium oxide content--CyDTA volumetric method
39 GB/T 5070.8-1985 镁铬质耐火材料化学分析方法硫酸亚铁铵容量法测定三氧化二铬量Magnesite-chrome refractories--Determination of chromium oxide content--Ammonium ferrous sulfate volumetric method
40 GB/T 5070.9-1985 镁铬质耐火材料化学分析方法原子吸收分光光度法测定氧化锰量Magnesite-chrome refractories--Determination of manganese oxide content--Atomic absorption spectrophotometric method
41 GB/T 5070.10-1985 镁铬质耐火材料化学分析方法原子吸收分光光度法测定氧化钾、氧化钠量Magnesite-chrome refractories--Determination of potassium oxide and sodium oxide contents--Atomic absorption spectrophotometric method
42 GB/T 5073-1985 耐火制品压蠕变试验方法Test method for creep in compression of refractory products
43 GB/T 5988-1986 致密定形耐火制品重烧线变化试验方法Dense shaped refractory products--Test method of linear changes on reheating
44 GB/T 5990-1986 定形隔热耐火制品导热系数试验方法(热线法) Shaped insulating refractory products--Test method of the thermal conductivity (hot wire method)
45 GB/T 6900.1-1986 粘土、高铝质耐火材料化学分析方法重量法测定灼烧减量Fireclay and high-alumina refractories--Determination of loss content on ignition--Gravimetric method
46 GB/T 6900.2-1986 粘土、高铝质耐火材料化学分析方法重量-钼蓝光度法测定二氧化硅量Fireclay and high-alumina refractories--Determination of silicon dioxide content--Gravimetric-molybdenum blue photometric method
47 GB/T 6900.3-1986 粘土、高铝质耐火材料化学分析方法邻二氮杂菲光度法测定三氧化二铁量Fireclay and high-alumina refractories--Determination of iron oxide content--o-Phenanthroline photometric method
48 GB/T 6900.4-1986 粘土、高铝质耐火材料化学分析方法EDTA容量法测定氧化铝量Fireclay and high-alumina refractories--Determination of aluminium oxide content--EDTA volumetric method
49 GB/T 6900.5-1986 粘土、高铝质耐火材料化学分析方法过氧化氢光度法测定二氧化钛量Fireclay and high-alumina refractories--Determination of titanium dioxide content--Hydrogen peroxide photometric method
50 GB/T 6900.6-1986 粘土、高铝质耐火材料化学分析方法EDTA容量法测定氧化钙量Fireclay and high-alumina refractories--Determination of calcium oxide content--EDTA volumetric method
51 GB/T 6900.7-1986 粘土、高铝质耐火材料化学分析方法二甲苯胺蓝I-溴化十六烷基三甲铵光度法测定氧化镁量Fireclay and high-alumina refractories--Determination of magnesium oxide content--Xylidyl blue I-CTAB photo-metric method
52 GB/T 6900.8-1986 粘土、高铝质耐火材料化学分析方法原子吸收分光光度法测定氧化钙、氧化镁量Fireclay and high-alumina refractories--Determination of calcium oxide and magnesium oxide content--Atomic absorpion spectrophotometric method
53 GB/T 6900.9-1986 粘土、高铝质耐火材料化学分析方法原子吸收分光光度法测定氧化钾、氧化钠量Fireclay and high-alumina refractories--Determination of potassium oxide and sodium oxide content--Atomic absorption spectrophotometric method
54 GB/T 6900.10-1986 粘土、高铝质耐火材料化学分析方法过硫酸铵光度法测定氧化锰量Fireclay and high-alumina refractories--Determination of manganese
oxide content--Ammonium persulfate photometric method
55 GB/T 6900.11-1986 粘土、高铝质耐火材料化学分析方法钼蓝光度法测定五氧化二磷量Fireclay and high-alumina refractories--Determination of phosphorus pentoxide content--Molybdenum blue photometric method
56 GB/T 6901.1-1986 硅质耐火材料化学分析方法重量法测定灼烧减量Silica refractories--Determination of loss content on ignition--Gravimetric method
57 GB/T 6901.2-1986 硅质耐火材料化学分析方法重量-钼蓝光度法测定二氧化硅量Silica refractories--Determination of silicon dioxide content--Gravimetric-molybdenum blue photometric method
58 GB/T 6901.3-1986 硅质耐火材料化学分析方法氢氟酸重量法测定二氧化硅量Silica refractories--Determination of silicon dioxide content--Hydrofluoric acid gravimetric method
59 GB/T 6901.4-1986 硅质耐火材料化学分析方法邻二氮杂菲光度法测定三氧化二铁量Silica refractories--Determination of iron oxide content--o-Phenanthroline photometric method
60 GB/T 6901.5-1986 硅质耐火材料化学分析方法铬天青S 光度法测定氧化铝量Silica refractories--Determination of aluminium oxide content--Chromazurol S photometric method
61 GB/T 6901.6-1986 硅质耐火材料化学分析方法EDTA容量法测定氧化铝量Silica refractories--Determination of aluminium oxide content--EDTA volumetric method
62 GB/T 6901.7-1986 硅质耐火材料化学分析方法二安替比林甲烷光度法测定二氧化钛量Silica refractories--Determination of titanium dioxide content--Diantipyrglmethane photometric method
63 GB/T 6901.8-1986 硅质耐火材料化学分析方法原子吸收分光光度法测定氧化钙、氧化镁量Silica refractories--Determination of calcium oxide content and magnesium oxide--Atomic absorption spectrophotometric method
64 GB/T 6901.9-1986 硅质耐火材料化学分析方法原子吸收分光光度法测定氧化钾、氧化钠量Silica refractories--Determination of potassium oxide and sodium oxide content--Atomic absorption spetrophotometric method
65 GB/T 6901.10-1986 硅质耐火材料化学分析方法原子吸收分光光度法测定氧化锰量silica refractories--Determination of manganese oxide content--Atomic absorption spectrophotometric method
66 GB/T 6901.11-1986 硅质耐火材料化学分析方法钼蓝光度法测定五氧化二磷量Silica refractories--Determination of phosphorus pentoxide content--Molybdenum
blue photometric method
67 GB/T 7320-1987 耐火制品热膨胀试验方法Test method for thermal expansion of refractory products
68 GB/T 7321-1987 致密定形耐火制品试验的制样规定Rule of preparing sample for tests of dense shaped refractory products
69 GB/T 8931-1988 耐火材料抗渣性试验方法Test method for the resistance of refractories to slag attack
70 GB/T 10324-1988 耐火制品的分型定义Refractory products--Definitions of model
71 GB/T 10325-1988 耐火制品堆放、取样、验收、保管和运输规则Refractory products--Instructions on stacking, sampling, acceptance, storage and transporting
72 GB/T 10326-1988 耐火制品尺寸、外观及断面的检查方法Refractory products--Inspections of dimension, appearance and section
73 GB/T 13243-1991 含碳耐火材料高温抗折强度试验方法Test method for modulus of rupture of refractories containing carbon at elevated temperatures
74 GB/T 13244-1991 含碳耐火材料抗氧化性试验方法Test method for oxidation resistance of refactories containing carbon
75 GB/T 13245-1991 含碳耐火材料化学分析方法燃烧重量法测定总碳量Chemical analysis method of refractories containing carbon—Determination of the total carbon—Combustion gravimetric method
76 GB/T 13246-1991 含碳耐火材料化学分析方法CyDTA 容量法测定氧化镁量Refractories containing carbon—Determination of magnesium oxide content—CyDTA volumetric method
77 GB/T 13794-1992 实验室用标准测温锥Pyrometric reference cones for laboratory use
78 GB/T 14350-1993 锆英石耐火材料化学分析方法Chemical analysis methods for zircon refractories
79 GB/T 14351-1993 熔铸氧化铝耐火材料化学分析方法Chemical analysis methods for fuse cast alumina refractories
80 GB/T 14982-1994 粘土质耐火泥浆Fireclay refractory mortars
81 GB/T 14983-1994 耐火材料抗碱性试验方法Test method for alkali-resistance of refractories
82 GB/T 15545-1995 不定形耐火材料包装、标志、运输和储存Unshaped refractory--Packing, marking, transportation and storage
83 GB/T 16546-1996 定形耐火制品包装、标志、运输和储存Shaped refractory
products--Packing, marking, transportation and storage
84 GB/T 16555.1-1996 碳化硅耐火材料化学分析方法吸收重量法测定碳化硅量Chemical analysis for silicon carbide refractories--Determination of silicon carbide--Absorb gravimetric method
85 GB/T 16555.2-1996 碳化硅耐火材料化学分析方法气体容量法测定碳化硅量Chemical analysis for silicon carbide refractories--Determination of silicon carbide--Gas volumetric method
86 GB/T 16555.3-1996 碳化硅耐火材料化学分析方法气体容量法测定游离硅量Chemical analysis for silicon carbide refractories--Determination of free silicon--Gas volumetric method
87 GB/T 16555.4-1996 碳化硅耐火材料化学分析方法EDTA容量法测定三氧化二铝量Chemical analysis for silicon carbide refractories--Determination of alumina--EDTA gas volumetric method
88 GB/T 16555.5-1996 碳化硅耐火材料化学分析方法邻二氮杂菲光度法测定三氧化二铁量Chemical analysis for silicon carbide refractories--Determination of ferric oxide--0-phenanthroline photometric method
89 GB/T 16555.6-1996 碳化硅耐火材料化学分析方法测定二氧化硅量Chemical analysis for silicon carbide refractories--Determination of silicon dioxide 90 GB/T 16763-1997 定形隔热耐火制品的分类Shaped insulating refractory products-classification
91 GB/T 5071-1997 耐火材料真密度试验方法Refractory materials-Determination of true density
92 GB/T 7322-1997 耐火材料耐火度试验方法Test method for pyrometric cone equivalent(refractoriness) of refractories
93 GB/T 17105-1997 致密定形耐火制品分类Classification of dense shaped refractory products
94 GB/T 17106-1997 耐火材料导热系数试验方法(平行热线法) Refractory materials--Determination of thermal conductivity--Hot-wire method(parallel)
95 GB/T 2273-1998 烧结镁砂Sintered magnesia
96 GB/T 17601-1998 致密定形耐火制品耐硫酸侵蚀性试验方法Dense shaped refractory products--Determination of resistance to sulfuric acid
97 GB/T 5072.1-1998 致密定形耐火制品常温耐压强度试验方法(无衬垫仲裁试验) Dense, shaped refractory products--Determination of cold compressive strength--Part 1: Referee test without packing
98 GB/T 2992-1998 通用耐火砖形状尺寸Dimensions of general bricks
99 GB/T 17617-1998 耐火原料和不定形耐火材料取样Refractory products--Sampling of raw materials and unshaped products
100 GB/T 3997.1-1998 定形隔热耐火制品重烧线变化试验方法Shaped insulating refractory products--Determination of permanent Change in dimension on heating 101 GB/T 3997.2-1998 定形隔热耐火制品常温耐压强度试验方法Shaped insulating refractory products--Determination of cold crushing strength
102 GB/T 5989-1998 耐火制品荷重软化温度试验方法(示差--升温法) Refractory products--Determination of Refractoriness-under-load(differential-with rising temperature)
103 GB/T 17732-1999 致密定形含炭耐火制品试验方法Dense, shaped refractory products--Test methods for products containing carbon
道路上行驶的汽车造型和性能特征等千差万别，如何区别这些汽车？一般来讲，根据新的汽车分类国家标准(gb9417-89)就可方便地区分车型。中国汽车划分为8大类： 1．载货汽车：依公路运行时厂定最大总质量（ga）划分为：微型货车（ga≤1．8吨）轻型货车（1．8吨＜ga≤6吨）中型货车（6．0吨＜ga≤14吨）重型货车（ga＞14吨）2．越野汽车：依越野运行时厂定最大总质量（ga）划分为：轻型越野汽车（ga≤5吨）中型越野汽车（5．0吨＜ga≤13吨）重型越野汽车（13＜ga≤24吨）超重型越野汽车（ga＞24吨） 3．自卸汽车：依公路运行时厂定最大总质量（ga）划分为：轻型自卸汽车（ga≤6吨）中型自卸汽车（6．0吨＜ga≤14吨）重型自卸汽车（ga＞14吨）矿山自卸汽车； 4．牵引车：半挂牵引车、全挂牵引车； 5．专用汽车：厢式汽车、罐式汽车、起重举升汽车、仓棚式汽车、特种结构式汽车、专用自卸汽车； 6．客车：依车长（l）划分为：微型（l≤3．5米）轻型（3．5米＜l≤7米）中型（7米＜l≤10米）大型客车（l＞10米）和特大型客车；中大型客车又可分为城市、长途、旅游及团体客车，特大型客车指铰接和双层客车； 7．轿车：依发动机排量（v）划分为：微型轿车（v≤1升）普通轿车（1升＜v≤1．6升）中级轿车（1．6升＜v≤2．5升）中高级轿车（2．5升＜v≤4升）高级轿车（v＞4升）8．半挂车：依公路运行时厂定最大总质量（ga）划分为：轻型半挂车（ga≤7．1吨）中型半挂车（7．1吨＜ga≤19．5吨）重型半挂车（19．5＜ga≤34吨）超重型半挂车（ga＞34吨）本站点车型定义与分类本网站主要收集小型客车,如各种轿车,轻型越野汽车,微型货车,微型客车。在中国，根据公安部的车辆分类标准,小型客车的共分为四类,即：·小轿车、越野车、旅行车、轻型小客车·本站点即主要采用这种分类办法。·本站点还同时收录适宜家庭使用的小型货车(皮卡,pickup),归类为小货车每辆车属于哪一种车型，请参阅该车的行驶证(不是司机驾驶证)正页第5行均已标明。·小轿车举例：桑塔纳，宝马，奥迪等；夏利、奥拓属于小轿车。切诺基小客车在北京行驶按照小轿车进
国家标准GB/T 13017修订编制说明 一、工作简况 1.任务来源 中国标准化研究院承担的国家标准GB/T 13017《企业标准体系表编制指南》（以下简称《指南》）的修订任务由中国标准化研究院提出，报国家标准化管理委员会批准，纳入国家标准化管理委员会制修订项目计划，编号为：53032Z-1101，项目代号20030435-T-424。 2.背景 《指南》于1991年发布后，曾于1995年第1次修订为V.2版，现为第2 次修订的V.3版。从V.2到目前即将发布的V.3的逾十年间，科学技术和标准都已呈现出巨大的发展与进步，使《指南》V.2版内容对照当前高新技术已显出很大的差距。首先，企业在面对瞬息万变的环境而又不能制定可预测的长期规划时，自身必须具有一种自然和动态的演进和适应能力，而不是偶然强加于企业的被动举动，这需要企业制订相应措施来应对。其次，我国目前在国民经济产值上虽然蒸蒸日上，但生产中的能耗、资源消耗、安全事故、劳动生产率、管理水平及在创新能力和国际竞争力上都居世界相当落后的地位，这对科学的管理体系提出了要求。再次，我国日益认识到标准的重要作用，起动了国家标准战略的研究，而企业的标准化是标准化战略的基础和落脚点。 3.主要工作过程 承接本标准的修订任务后,我院早在2003年就成立了的标准修订课题组，并去上海汽车工业（集团）公司和宝钢集团做了调研工作，在鲍仲平同志的直接指
导和亲自带领下，收集了大量标准和文献，做了充分的前期调研工作。经过课题组的努力,2006年初基本完成了本标准的草案稿，3月向本院的院领导及各研究所做了汇报，相继走访了多家企事业单位，深入听取了各方意见；并对草案做了多次修改，于2006年6月完成了本标准的征求意见稿。 二、内容简介 1.本标准的定位 a）为编制先进、科学的企业标准体系提供指导 《指南》第三版采纳并融合了国际上最新管理理念和高技术水平的标准。 b）面向所有企业的中性标准 定位在实施系统集成的现代化企业集团，同时也适用于不实施这些集成 的传统企业。既适合于制造业企业，也适用于服务业等其他企业，也可 以为政府电子政务项目建立标准体系提供指导。 2.技术创新 a）以企业建模标准体系（企业工程和集成标准体系）为指导ISO发布了企业建模的系列标准，包括“通用企业参考体系结构与方法 论”GERAM，其范围包括企业工程/企业集成所需的所有知识。要求把 改变过程中利用的多种学科的方法统一起来，例如工业工程、管理科学、 通信和信息技术等方法。GERAM框架的目的是要把基于产品模型和基 于业务过程设计的两种不同的企业工程方法统一起来。 b）以企业管理体系为指导 ISO已发展和制定出“质量管理体系”“环境管理体系”“职业健康安全 管理体系”“信息安全管理”等成套的标准体系，此外还有“风险管理”、
《车用汽油》国家标准 征求意见稿编制说明 1任务来源 依据国家标准化管理委员会下发的国标委综合[2012]25号“关于下达《车用汽油》等2项国家标准制修订项目的通知”，由中国石油化工股份有限公司石油化工科学研究院负责对修订《车用汽油》国家标准。项目编号：20120002-Q-469。 2目的和意义 近年来，国民经济的高速发展带动了国内汽车工业的发展。根据资料显示，2010年我国汽车的产量达到1826万辆，占到世界汽车总产量的23.5%。汽车的大量使用，在给人们的出行带来便捷的同时，也给大气质量造成一定的影响，汽车排放的污染物分担率不断上升，为此，为了降低机动车的排放污染物数量，改善大气环境，中国目前正在制定我国未来第V阶段的汽车排放法规。为了满足这一更加严格的排放要求，需要高质量的车用汽油与之相配套。 本标准在GB 17930-2011《车用汽油》附录A的基础上，参考了2012年北京市制定第V阶段地方标准时所做的一些研究工作，对某些指标进行适当的调整。 3 标准的编制过程及强制理由 本标准依据国家标准化管理委员会2012年4月27日下发的国标委综合[2012]25号“关于下达《车用汽油》等2项国家标准制修订项目的通知”，由中国石油化工股份有限公司石油化工科学研究院负责修订GB 17930-2011《车用汽油》国家标准。 2012年5-6月，接到任务后，课题组首先对国内相关标准的变化情况和国外标准的现状以及目前国内炼厂的状况开展调研。由于本次标准制定的时间要求非常急迫，难于遵循过去在GB 17930-2006和GB 17930-2011起草中所采用的研究方法，为此经课题组研究，本标准在GB 17930-2011《车用汽油》附录A的基础上，参考北京
1．设计指标：statistics 用地面积：site area 建筑占地面积：building foot print 总建筑面积：total area 建筑面积floor area，building area 地上建筑面积：ground area 地下建筑面积：underground area 整体面积需求: Demand for built area 公共绿地：public green land 备用地用地：reserved land 容积率：FAR 建筑密度：building coverage 绿地率：green ratio 绿化率：green landscape ratio 建筑高度：building height 层数：number of floors 停车位：parking unit 地面停车：ground parking 地下停车：underground parking 使用面积：usable area 公用面积：public area 实用面积：effective area 居住面积：living area 计租面积rental area?租用面积 得房率：effien 开间bay 进深depth 跨度span 坡度：slope，grade 净空：clearance 净高：clear height 净空（楼梯间下）：headroom 净距：clear distance 套内面积：unit constraction area 公摊面积：shared public area 竣工面积： 辅助面积：service area 结构面积：structural area 交通面积：communication area，passage area 共有建筑面积：common building area 共有建筑面积分摊系数：common building area amount coefficient 公用建筑面积：public building area 销售面积：sales area 绿化覆盖率：green coverage ratio 层高：floor height 净高：clear height 公用建筑面积分摊系数：public building area amount coefficient 住宅用地：residential area 其他用地： 公共服务设施用地：land for public facilities 道路用地：land for roads 公共绿地：public green space 道路红线：road property line 建筑线（建筑红线）：set back line 用地红线：property line，boundary line 第一轮：1st round 计划和程序：schedule and program 工程进度表：working schedule 构造材料表：list of building materials and construction 设计说明：design statement 图纸目录和说明：list of drawings and descriptions 项目标准：project standards 总结：conclusion 文本及陈述： 封皮：cover 目录：content 技术经济指标：technical and economical index 概念规划设计：conceptual master paln and architectural design 基地分析：location analysis 项目区位分析图：description of the region site and city space view analyze 概念构思说明：chief design concept 指导思想（设计主旨）：key concepts 概述：introduction 宗旨：mission statement 愿景及设计效果：vision and design concept 城市空间景观分析：urban space landscape identity 绿化景观分析：landscape analysis 交通分析：traffic analysis 生态系统：ecological system 地块A：area A 模型照片：model images 案例分析：case study
耐火制品 耐火粘土砖 Fire Clay Brick 规格：由买方选择 包装：托盘，约1.2吨 用途：适用于高炉、焦炉、加热炉、盛钢桶、浇钢砖、有色冶金炉、水泥窑、玻璃窑及烟囱等各种窑炉与热工设备。 产地：山东、山西、河北、河南、辽宁、北京、上海、天津等地。
Specifications:At Buyer's Option. Uses:suitable for blast furnace,coke oven,preheating furnace,ladle lining,steel teeming,non- ferrous metallurgical furnace,boiler,cement l\kiln,glass tands,chimney and other kilns or furnaces and heat equipment. Packing:in wooden pallet,about1.2MT each pallet. Place of Origin:Shandong,Shangxi,Hebei,Henan,Liaoning,Shanghai,Tianjin,etc. 高铝砖 High Alumina Brick 规格：由买方选择 包装：托盘 用途：适用于电炉炉顶、高炉、加热炉、盛钢桶、铁水车、水泥窑、玻璃窑及烟囱及其他高温窑炉产地：山西、河南、河北、山东、北京、上海、天津等地。 Specifications:At Buyer's Option. Uses: suitable for roof of electric arc furnace, preheating furnace, ladle lining, torpedo, cement kiln, glass tank, other furnaces and kilns at high temperature. Paking:ln wooden pallet. Place of Origin:Shandong,Shangxi,Hebei,Henan,Liaoning,Shanghai,Tianjin,etc. 铝碳化硅碳砖 规格：由买方选择 用途：鱼雷车内衬、铁水包内衬 Specifications:At Buyer's Option. Uses:Torpedor lining and iron ladle lining.
中华人民共和国国家标准 锅炉用水和冷却水分析方法 钠的测定动态法GB12155—89 Analysis of water used in boiler and cooling system-Determination for sodium-Dynamic method 国家技术监督局1989-12-29批准1990-11-01实施 1 主题内容与适用范围 1.1 主题内容 本标准规定了水中钠离子含量的动态测定法。 1.2 适用范围 本标准适用于除盐水、发电厂锅炉给水、蒸汽、凝结水等水样中微量钠离子的测定，测范围为0～2300μg/L。 2 引用标准 GB 6903 锅炉用水和冷却水分析方法通则 3 方法提要 当钠离子选择电极——pNa电极与甘汞参比电极同时浸入溶液后，即组成测量电池对，其中pNa电极的电位随溶液中钠离子的活度而变化。用一台高阻抗输入的毫伏计测量，即可获得与水样中钠离子活度相对应的电极电位，以pNa值表示： pNa=-lg Na+ a b (1) pNa电极的电位与溶液中钠离子活度的关系符合能斯特公式： E E RT nF a = 0+2.3026lg Na+ (2) 式中E——pNa电极所产生的电位，V； E0——当钠离子活度为1mol/L时，pNa电极所产生的电位，V； R——气体常数，8.314J·K-1·mol-1； T——热力学温度，K； F——法拉第常数，9.649×104C·mol-1； n——参加反应的得失电子数； a Na+——溶液中钠离子的活度，mol/L。 当溶液中钠离子浓度小于10-3mol/L时，钠离子活度近似等于浓度，离子活度系数γ≈1。当钠离子浓度大于10-3mol/L时，离子活度系数γ≠1。在测定中要注意活度系数的修正，为此，水样应预先稀释，否则误差较大。 当测定溶液的ＣNa+<10-3mol/L，被测溶液和定位溶液的温度为20℃，则式(2) 可简化为： 00581g . ' = C C E Na Na + + ?(3) 0058 .(pNa-pN a)'=?E(4)
船体结构中英文对照表！！ 中英文对照船体结构 主船体main hull 上层建筑superstructure 上层连续甲板upper deck 船底bottom 舷侧broadside 艏艉fore and aft 舱壁bulkhead 水密watertight 艏部bow 艉部stern/quarter 二层甲板second deck 平台甲板platform deck 桅屋masthouse 罗经甲板compass deck 驾驶甲板bridge deck 船长甲板master deck 高级船员甲板office deck 艇甲板boat deck 船员甲板crew deck 机舱engine room 货舱cargo hold 货舱口cargo hatch
压载舱ballast tank 深舱deep tank 燃油舱fuel oil tank 滑油舱lubricating oil tank 淡水舱fresh water tank 污油水舱slop tank 隔离空舱/干隔舱caisson 球鼻艏标志bulbous bow mark/BB mark 首侧推器标志 bow thruster mark/BT mark 吃水标志draft mark 甲板线deck line 干舷甲板freeboard deck 载重线标志load line mark 热带淡水载重线 tropical fresh water load line/TF 夏季淡水载重线 fresh water load line/F 热带载重线 tropical load line/T 夏季载重线 summer load line/S 冬季载重线winter load line 北大西洋冬季载重线 winter North Atlantic load line/WNA 国际船舶载重线证书 international load line certificate 吃水指示系统 draft indicating system 船舶尺度ship dimension 最大尺度/全部尺度/周界尺度 overall dimension 最大长度/全长/总长 length overall/LOA 最大宽度/全宽 extreme breadth
最新国家标准公文格式（2013年） 标题（2号小标宋体） 发文对象：（标题下一行顶格，3号仿宋） X X X X X X X X X X（正文3号仿宋体字） 一、X X X(黑体) X X X X X X X X X X（正文3号仿宋体字） （一）X X X（楷体） X X X X X X X X X X（正文3号仿宋体字） 1.X X X仿宋 X X X X X X X X X X（正文3号仿宋体字） （1）X X X仿宋 X X X X X X X X X X X（正文3号仿宋体字） 附件：1.X X X(正文下一行右空两字) 2.X X X 单位名称（附件下两行居成文日期中） 成文日期（右空四字，用阿拉伯数字）（联系人：……；联系电话：……）（如有附注，居左空二字加圆括号编排在成文日期下一行。）
(说明)1.标题：一般用2号小标宋体字，分一行或多行居中排布；回行时，要做到词意完整，排列对称，长短适宜，间距恰当，标题排列应当使用梯形或菱形。 2.正文：一般用3号仿宋体字，每个自然段左空二字，回行顶格。文中结构层次序数依次可以用“一、”“（一）”“1.”“（1）”标注；一般第一层用黑体字、第二层用楷体字、第三层和第四层用仿宋体字标注。 3.附件：如有附件，在正文下空一行左空二字编排“附件”二字，后标全角冒号和附件名称。如有多个附件，使用阿拉伯数字标注附件顺序号（如“附件：1. XXXXX”）；附件名称后不加标点符号。附件名称较长需回行时，应当与上一行附件名称的首字对齐。 附件应当另面编排，并在版记之前，与公文正文一起装订。“附件”二字及附件顺序号用3号黑体字顶格编排在版心左上角第一行。附件标题居中编排在版心第三行。 4.发文机关署名：单一机关行文时，在正文（或附件说明）下空一行右空二字编排发文机关署名，在发文机关署名下一行编排成文日期，首字比发文机关署名首字右移二字，如成文日期长于发文机关署名，应当使成文日期右空二字编排，并相应增加发文机关署名右空字数。 5. 成文日期中的数字：用阿拉伯数字将年、月、日标全，年份应标全称，月、日不编虚位（即1不编为01）。 6.页码：一般用4号半角宋体阿拉伯数字，编排在公文版心下边缘之下，数字左右各放一条一字线；一字线上距版心下边缘7 mm。单页码居右空一字，双页码居左空一字。公文的版记页前有空白页的，空白页和版记页均不编排页码。公文的附件与正文一起装订时，页码应当连续编排。 此样式根据2012《党政机关公文格式国家标准》编写而成，标准中未提及具体行距，一般公文中标题行距28磅。正文及其他单倍行距。如有不当请指正。
B/T3730.1-1998汽车和半挂车的术语及定义车辆类型 GB/T3730.3-1992汽车和半挂车的术语及定义车辆尺寸 GB/T3730.2-1996道路车辆质量词汇和代码 GB/T17347-1998商用道路车辆尺寸代码 GB/T16735-1997道路车辆车辆识别代号(VIN)位置及固定 GB/T16736-1997道路车辆车辆识别代号(VIN)内容与构成 GB/T16737-1997道路车辆世界制造厂识别代号(WMI) GB/T16738-1997道路车辆世界零件制造厂识别代号(WPMI) GB/T17349.1-1998道路车辆汽车诊断系统词汇 GB/T4782-1984道路车辆-操纵件、指示器及信号装置-词汇 GB/T4971-1985汽车平顺性名词术语和定义 GB/T12549-1990汽车操纵稳定性术语及其定义 GB/T15089-1994机动车辆分类 QC/T34-1992汽车的故障模式及分类 QC/T571-1999汽车清洁度工作导则名词、术语 GB/T9417-1988汽车新产品型号编制规则 GB/T17349.2-1998道路车辆汽车诊断系统图形符号 GB4094-1999汽车操纵件指示器及信号装置的标志 GB/T17676-1999天然气汽车和液化石油气汽车标志 GB/T4781-1984牵引车与全挂车的机械连接装置互换性 GB/T4606-1984道路车辆半挂车鞍座50号牵引销主要尺寸和安装互换性尺寸GB/T4607-1984道路车辆半挂车鞍座90号牵引销主要尺寸和安装互换性尺寸QC/T538-1999载货汽车燃料消耗量限值 QC/T535-1999重型载货汽车燃料消耗量限值 GB1495-1979机动车辆允许噪声 GB16170-1996汽车定置噪声限值 GB1589-1989汽车外廓尺寸限界 GB11561-1989汽车加速器控制系统的技术要求 GB11553-1989汽车正面碰撞时对燃油泄漏的规定 GB/T7031-1986车辆振动输入路面平度表示方法 GB7258-1997机动车运行安全技术条件 GB17259-1998机动车用液化石油气钢瓶 GB17258-1998汽车用压缩天然气钢瓶 QC/T245-1998压缩天然气汽车专用装置和安装要求 QC/T247-1998液化石油气汽车专用装置和安装要求 QC/T251-1998矿用自卸汽车应急转向性能要求 GB/T16887-1997卧铺客车技术条件 QC/T635-2000双层客车技术要求
Black silicon carbide Black silicon carbide is produced at high temperature in an electric resistance type furnace with quarts sand and petroleum coke as its main raw materials. Its hardness is between fused alumina and synthetic diamond. Mechanical intensity of it is higher than fused alumina. It is brittle and sharp has electrical and heat conductivity in some degree. The abrasives made of it are suitable for working on cast iron, non-ferrous metal, rock, leather, rubber, etc. It is also broadly used as refractory material and metallurgical additive. 黑色碳化硅产生在高温下的电阻型炉用石英砂，石油焦为主要原料。 其硬度介于刚玉和合成金刚石之间。它的机械强度高于刚玉。这是性脆而锋利具有电气和热导率在一定程度上。 用其制成的研磨剂适用于加工铸铁，非铁金属，石头，皮革，橡胶等，还广泛用于耐火材料，冶金添加剂。 Green silicon carbide Suitable for processing hard metal alloys and non-metallic materials that are hard and brittle such as jewels, optical glass or ceramics. It's sharp cuting characteristics also make it useful for soft materials such as copper, brass, aluminium or magnesium. Used as vitrified wheels and belts, organic wheels, and sheets. Applicated for refractory industry. Super micropowder from green silicon carbide can be used to make a kind of ceramic material. Also used for wire sawing, semi conductor material. 适合于加工硬金属合金和非金属材料是硬而脆的，如珠宝，光学玻璃或陶瓷。 它的锋利切削特性也使它可用于软质材料，如铜，黄铜，铝或镁。 作为陶瓷结合剂砂轮和腰带，有机轮，和床单。 一种实用性为耐火材料行业。 从绿色碳化硅超级微粉可以用来制作一种陶瓷材料构成。 也可用于绳锯，半导体材料。 Brown fused alumina 1. Description: Brown aluminium oxide/brown fused alumina is fused and crystallized under high temperature from a mixture of bauxite and other and other raw materials. It is characterized by its high hardness,good toughness and shape in size. Abrasives tools made of it are suitable for grinding metals of high-tensile strength such as: carbon steel,general-purpose alloy steel,annealed malleable iron and hard broze,etc. It also can be used as refractory materials. 2. Application: ?Suitable for grinding high-speed,high carbon steel ?High-grade refractory materials ?Abrasives tool ?Grinding and polishing ?Ceramics ?LED ?Sandblasting ?Aviation 1。描述：棕刚玉/棕刚玉是由铝矾土等及其他原料的混合物熔融，并在高温下结晶。它的特点是其高硬度，良好的韧性和形状的大小。用它制成的磨具适用于磨削高抗拉强度的金属，如：碳素钢，通用合金钢，可锻铸铁，硬broze等。它也可以用来作为耐火材料。 2。应用： ?适用于磨削高速，高碳钢?高档耐火材料?磨料工具?研磨和抛光?陶瓷?LED ?喷砂?航空
国家标准、规范、规程国家标准、规范、规程(2011) (2011)目录（录（截止日期截止日期2011.10.12011.10.1） ）一标准规范 (1) 1工程建设国家标准GB ...................................................12工程建设行业标准JGJ .................................................253城镇建设行业标准CJJ .................................................354工程建设标准化协会标准CECS ....................................415工程建设材料、设备国家标准GB，JG，CJ，JC ........526公路标准.........................................................................57二国家建筑标准设计图集 (58) 1全国民用建筑工程设计技术措施、深度规定..............582建筑专业J .....................................................................593结构专业G .....................................................................634给水排水专业S .............................................................685暖通空调专业K .............................................................716动力专业R .....................................................................727电气专业D .....................................................................748弱电专业X .....................................................................759城市道路MR ...................................................................7510市政给水排水MS .........................................................76三特种设备 (76) 1安全技术规范TSG .........................................................762锅容标委归口行业标准及图书.....................................793国家标准GB ...................................................................80四企业标准..............................................................................85五其它行业标准. (85) 1化工工程建设HG ...........................................................852石化工程建设SH .. (86) 一标准规范
中华人民共和国国家标准 汽车维护、检测、诊断技术规范 GB/T 18344－2001 1 范围 本标准规定了汽车日常维护、一级维护、二级维护的周期，作业内容和技术规范。 本标准适用于所有在用汽车。 2 引用标准 下列标准所包含的条文，通过在本标准中引用而构成为本标准的条文。本标准出版时，所示版本均为有效。所有标准都会被修订，使用本标准的各方应探讨使用下列标准最新版本的可能性。 GB7258－1997机动车运行安全技术条件 3 定义 本标准采用下列定义 3.1 日常维护routine maintenance 以清洁、补给和安全检视为作业中心内容，由驾驶员负责执行的车辆维护作业。 3.2 一级维护elementary maintenance 除日常维护作业外，以清洁、润滑、紧固为作业中心内容。并检查有关制度、操纵等安全部件，由维修企业负责执行的车辆维护作业。 3.3 二级维护complete maintenance 除一级维护作业外。以检查、调整转向节、转向摇臂、制动蹄片、悬架等经过一定时间的使用容易磨损或变形的安全部件为主，并拆检轮胎，进行轮胎换位，检查调整发动机工作状况和排气污染控制装置等，由维修企业负责执行的车辆维护作业。 4 汽车维护分级和周期
4.1 汽车维护的分级 日常维护，一级维护，二级维护。 4.2 汽车维护的周期 4.2.1 日常维护的周期 出车前，行车中，收车后。 4.2.2 一级维护、二级维护的周期 4.2.2.1 汽车一、二级维护周期的确定，应以汽车行驶里程为基本依据。 汽车一、二级维护行驶里程依据车辆使用说明书的有关规定，同时依据汽车使用条件的不同，由省级交通行政主管部门。 4.2.2.2 一、二级维护时间间隔。 对于不便用行程里程统计、考核的汽车，可用行驶时间间隔确定一、二级维护周期。其时间（天）间隔可依据汽车使用强度和条件的不同。参照汽车一、二级维护里程周期确定。 5 日常维护 5.1 对汽车外观、发动机外表进行清洁，保持车容整洁。 5.2 对汽车各部润滑油（脂）、燃油、冷却液、制动液、各种工作介质、轮胎气压进行检视补给。 5.3 对汽车制动、转向、传动、悬挂、灯光、信号等安全部位和位置以及发动机运转状态进行检视、校紧，确保行程安全。 6 一级维护 一级维护作业内容见表1。 表1 一级维护作业内容
。 最新国家标准公文格式 标题（2号小标宋体） 发文对象：（标题下一行顶格，3号仿宋） X X X X X X X X X X（正文3号仿宋体字） 一、X X X(黑体) X X X X X X X X X X（正文3号仿宋体字） （一）X X X（楷体） X X X X X X X X X X（正文3号仿宋体字） 1.X X X仿宋 X X X X X X X X X X（正文3号仿宋体字） （1）X X X仿宋 X X X X X X X X X X X（正文3号仿宋体字） 附件：1.X X X(正文下一行右空两字) 2.X X X 单位名称（附件下两行居成文日期中） 成文日期（右空四字，用阿拉伯数字）（联系人：……；联系电话：……）（如有附注，居左空
二字加圆括号编排在成文日期下一行。） (说明)1.标题：一般用2号小标宋体字，分一行或多行居中排布；回行时，要做到词意完整，排列对称，长短适宜，间距恰当，标题排列应当使用梯形或菱形。 2.正文：一般用3号仿宋体字，每个自然段左空二字，回行顶格。文中结构层次序数依次可以用“一、”“（一）”“1.”“（1）”标注；一般第一层用黑体字、第二层用楷体字、第三层和第四层用仿宋体字标注。 3.附件：如有附件，在正文下空一行左空二字编排“附件”二字，后标全角冒号和附件名称。如有多个附件，使用阿拉伯数字标注附件顺序号（如“附件：1. XXXXX”）；附件名称后不加标点符号。附件名称较长需回行时，应当与上一行附件名称的首字对齐。 附件应当另面编排，并在版记之前，与公文正文一起装订。“附件”二字及附件顺序号用3号黑体字顶格编排在版心左上角第一行。附件标题居中编排在版心第三行。 4.发文机关署名：单一机关行文时，在正文（或附件说明）下空一行右空二字编排发文机关署名，在发文机关署名下一行编排成文日期，首字比发文机关署名首字右移二字，如成文日期长于发文机关署名，应当使成文日期右空二字编排，并相应增加发文机关署名右空字数。 5. 成文日期中的数字：用阿拉伯数字将年、月、日标全，年份应标全称，月、日不编虚位（即1不编为01）。 6.页码：一般用4号半角宋体阿拉伯数字，编排在公文版心下边缘之下，数字左右各放一条一字线；一字线上距版心下边缘7 mm。单页码居右空一字，双页码居左空一字。公文的版记页前有空白页的，空白页和版记页均不编排页码。公文的附件与正文一起装订时，页码应当连续编排。 此样式根据2012《党政机关公文格式国家标准》编写而成，标准中未提及具体行距，一般公文中标题行距28磅。正文及其他单倍行距。如有不当请指正。
中华人民共和国国家标准GB/T18894-2002 电子文件归档与管理规范 1 范围 本标准规定了在公务活动中产生的，具有保存价值的电子文件的形成、积累、归档、保管、利用、统计的一般方法。 本标准适用于党政机关产生的电子文件的归档与管理，其他社会组织的电子文件管理可参照本标准。 2 规范性引用文件 下列文件中的条款通过本标准的引用而成为本标准的条款。凡是注日期的引用文件，其随后所有的修改单(不包括勘误的内容)或修订版均不适用于本标准，然而，鼓励根据本标准达成协议的各方研究是否可使用这些文件的最新版本。凡是不注日期的引用文件，其最新版本适用于本标准。 DA／T 18档案著录规则 DA／T 22归档文件整理规则 3 术语和定义 下列术语和定义适用于本标准。 3.1 电子文件electronic records 指在数字设备及环境中生成，以数码形式存储于磁带、磁盘、光盘等载体，依赖计算机等数字设备阅读、处理，并可在通信网络上传送的文件。 3.2 归档电子文件archival electronic records 指具有参考和利用价值并作为档案保存的电子文件(3.1)。 3.3 背景信息context 指描述生成电子文件(3.1)的职能活动、电子文件的作用、办理过程、结果、上下文关系以及对其产生影响的历史环境等信息。 3.4 元数据metadata 指描述电子文件(3.1)数据属性的数据，包括文件的格式、编排结构、硬件和软件环境、文件处理软件、字处理和图形工具软件、字符集等数据。 3.5 逻辑归档logical filing 指在计算机网络上进行，不改变原存储方式和位置而实现的将电子文件(3.1)的管理权限向档案部门移交的过程。 3.6 物理归档physical filing 指把电子文件(3.1)集中下载到可脱机保存的载体上，向档案部门移交的过程。 3.7 真实性authenticity 指对电子文件(3.1)的内容、结构和背景信息(3.3)进行鉴定后，确认其与形成时的原始状况一致。3.8 完整性integrity 指电子文件(3.1)的内容、结构、背景信息(3.3)和元数据(3.4)等无缺损。 3.9 有效性utility
锅炉一般术语 Spray coating喷涂 Water feeder（锅炉）给水设备Water treated（锅炉）水处理设备Ventilation Equipment（锅炉）通风设备 E type midspeed coal milling E型中速磨煤机Safety valve安全阀 Safety stop device安全停车装置 Safety relief valve安全泄放阀 safety device安全装置 Babbitt metal巴氏合金 apron self-loading scraper扒斗机 slagging-off扒渣 Cinguefoil brick白云石砖 Grille screen百格网 semi-opened impeller半开式燃烧室 pusher furnace半连续炉semispherical combustion chamber半球形燃烧室 1/2 Width半条 Half-bat半砖（半块） Wrap pipe包墙管 Journal sticking抱轴 Pop-in crack phenomenon爆皮现象法 Bainite贝氏体Austempering贝氏体等温淬火Standard scraper标准式铲运机Parallel operation并车 Parallel operation test并车试验 Glass cotton玻璃棉 thin walled half bearing薄壁轴瓦 Lamina薄片 Made-up water补给水 Make-up-expanding补胀 Uncertain sized refractory不定形耐火材料Partial annealing, incomplete annealing不完全退火 Walking beam furnace步进式炉 Scratching擦伤 Overall material utilization factor材料利用率 Residual gas残余氢 Lateral lay侧砌 Lateral quoin brick侧楔形砖（刀口砖）Measure temperature dot测温点（烘炉测温点）Measure pressure dot测压点（烘炉测压点）Staff with level mark层线杆（竖标杆）Flashboard插板 Superhigh pressure boiler超高压锅炉
压力表国家标准 中华人民共和国国家标准GB/T 1227-2002 标准压力表,精密压力表于2002-1-25发布 2003-05-01实施。该标准由中华人民共和国国家质量监督检验检疫总局发布，共有七个部分，另附一个规范性附录和两个资料性 目录。国标 GB/T 1227-2002 精密压力表代替原精密压力表国家标准 GB/T 1227-1986 标准精密压力表。国标GB/T 1227-2002 精密压力表涉及的相关标准有：GB/T 4439-1984 工业自动化仪表工作条件振动；GB/T 4451-1984 工业自动化仪表振动（正弦）试验方法；GB/T 15464 仪器仪表包装通用技术条件；JB/T 5528 压力表标度及划分；JB/T 9252 工业自动化仪表指针指示部分的基本型式、尺寸及指针的一般技术要求；JB/T 9253 工业自动化仪表标度的一般规定；JB/T 9329-1999 仪器仪表运输、运输储存基本环境条件及试验方法。 中华人民共和国国家标准 GB/T 1227-2002《精密压力表》规定了精密压力表的产品分类、技术要求、试验方法、检验规则和标志、包装与贮存。GB/T 1227-2002《精密压力表》国家标准适用于以C型管式弹簧管、盘簧管式弹簧管、螺旋管式弹簧管等弹性敏感元件为测量部件的机械指针式精密压力表。 GB/T 1227-2002《精密压力表》解读[1]产品分类与技术要求 中华人民共和国国家标准 GB/T 1227-2002《精密压力表》中规定了精密压力表型式的产品分类: 精密压力表按其测量类别分为压力表和真空表，所谓测量类别是指精密压力表测量范围所属的量域是正压或是负压。另 外还有一种跨量域的精密压力真空表已在工业流程中广为应用，GB/T 1227-2002《精密压力表》暂未将其列入测量分类之中。精密压力表按其安装方式分为直接安装式和嵌装式。所谓安装方式是指精密压力表自身所具有的 安装结构型式。直接安装式是应用较多的一种典型安装结构型式，其接口螺纹既要起到管路的连接作用又要起 到对仪表的支撑作用。嵌装式也称盘装式，是一种带有安装环的精密压力表。也就是我们常说的轴向前带边精 密压力表和径向前带边精密压力表。此类仪表的安装环是仪表的支撑部件，其接口螺纹只起着管路连接作用。 还有一种安装结构型式─凸装式，也就是我们常说的后带边精密压力表，也有称其为墙装式，这种凸装式精密 压力表的应用也较普遍，GB/T 1227-2002《精密压力表》也暂未将其列入安装方式之中。 中华人民共和国国家标准 GB/T 1227-2002《精密压力表》中明确规定了精密压力表的精确度等级产品分类。所谓精密压力表的精确度等级，也就是常说的精度等级。精密压力表的精确度等级分为：级；级；级；级。精 确度等级是精密压力表的主要技术指标之一，它表示了精密压力表的测量精度。 中华人民共和国国家标准 GB/T 1227-2002《精密压力表》中规定了精密压力表基本参数的产品分类。 基本参数 1.精密压力表外壳公称直径（mm）系列：Φ150、Φ200、Φ250、Φ300、Φ400。 基本参数2.精密压力表测量范围的上限（MPa）应符合规定的系列：1×10n、×10n、×10n、4×10n、 6×10n。